Cobalt base alloys as well as Ni+WC
Cobalt base alloys as well as Ni+WC .Their low melting points, low
oxygen and impurities result in porosity-free, fine-grained structures with superior wear and
corrosion resistance
| Cobalt Alloys | |||||||||||||
| Powder | HRC | Chemical Composition | Mesh | Coating Process | |||||||||
| C | Cr | Si | B | Fe | Mo | Ni | Co | Mn | W | ||||
| Co21LA | 35 | 0.30 | 26.00 | 0.50 | – | 1.00 | 6.00 | 4.00 | Bal | 1.00 | – | 100/270 or 150/300 |
Laser Cladding |
| Co22C | 40 | 0.50 | 25.00 | 0.50 | – | 1.00 | 12.00 | 3.50 | Bal | 1.00 | – | ||
| Co25 | 340 | 0.25 | 27.00 | 1.00 | – | 1.50 | 5.50 | 2.80 | Bal | 0.50 | – | ||
| CoX-40 | 35 | 0.85 | 24.10 | 0.30 | 1.30 | 1.50 | 0.40 | 8.50 | Bal | 0.50 | 7.50 | ||
| Co06 | 40 | 1.10 | 28.50 | 1.10 | 2.60 | 1.50 | – | 1.50 | Bal | 0.50 | 4.40 | ||
| Co06H | 45 | 1.30 | 28.50 | 1.00 | 0.90 | 1.50 | – | 1.50 | Bal | 0.50 | 4.40 | ||
| CoFH | 40 | 1.70 | 26.00 | 1.20 | – | 1.20 | – | 22.00 | Bal | 0.50 | 12.50 | ||
| Co12 | 48 | 1.40 | 28.50 | 1.10 | – | 1.00 | – | 1.50 | Bal | 0.50 | 8.00 | ||